T-PRIME 130 - EPOXY TOOLING INFUSION SYSTEM
- Thermally stable up to 130°C / 266°F when fully post-cured
- Resistant to thermal cycling damage
- Low initial mixed viscosity for easier infusion; 247 cP at 25°C / 77°F
- Long pot-life and gel time; capable of infusing large or complex moulds
- Ambient curing and low shrinkage for accurate mould manufacture
T-Prime 130-1 is an epoxy tooling system for manufacturing glass or carbon moulds from liquid infusion processes. T-Prime 130-1 is compatible with Gurit’s range of 130°C tooling gelcoat, laminating and repair systems.
T-Prime 130-1 is a low shrinkage ambient curing system, which provides a simple way to produce high accuracy moulds. Designed for infusion and cure at ambient temperatures, it should then be mid-cured at 40°C / 104°F for 4 hours to guarantee the strength needed for demoulding. It can then be postcured off the plug to give a material that is thermally stable to 130°C / 266°F.
Exceeding this temperature will cause a rapid loss in stiffness and a safety margin is required for the maximum tool operating temperature to prevent distortion or tool damage.
T-Prime 130-1 is a further improvement on T-Prime 130 giving improved storage stability and an extended pot-life.
| T-PRIME 130-1 - 20 kg |
|
|
Resin
|
Article
|
|
12,5 Kg
|
T-PRIME130-RC
|
|
|
Hardener
|
Typ
|
Article
|
|
3,4 Kg
|
Standard
|
T-PRIME130-HC
|
|
| |
|
| T-PRIME 130-1 - 185 kg |
|
|
Resin
|
Article
|
|
185 Kg
|
T-PRIME130-RD
|
|
|
Hardener
|
Typ
|
Article
|
|
16,7 Kg
|
Standard
|
T-PRIME130-HD
|
|